Method of making shaped activated carbon

ABSTRACT

A new shaped activated carbon and the method of its manufacture are disclosed. The invention resides in the crosslinking of a polymeric cellulose, such as sodium carboxymethylcellulose (CMC), within the carbon bodies after they are shaped, employing the CMC as a binder for the activated carbon. The approach to attain product mechanical strength and water stability by crosslinking rather than high temperature heat treatment is not obvious from the prior art teaching. The crosslinking reaction occurs at temperatures below 270° C. In addition, this new binder technology produces shaped carbon bodies having key properties beyond the best level that has been accomplished with other binders.

[0001] This invention relates to activated carbon. In addition, this invention relates to shaped activated carbon formed from powdered activated carbon. This invention also relates to shaped activated carbon formed from powdered activated carbon and a binder material.

BACKGROUND

[0002] Activated carbons are extensively used to purify, decolorize, deodorize, dechlorinate, and detoxicate potable waters; for solvent recovery and air purification in inhabited spaces such as restaurants, food-processing, and chemical industries; in the purification of many chemical and foodstuff products; and in a variety of gas phase applications. Activated carbons are of interest in many economic sectors and concern industries as diverse as food processing, pharmaceuticals, chemical, petroleum, mining, nuclear, automobile, and vacuum manufacturing. In particular, characterization of the carbon surface and its porous structure with respect to the chemical composition of the surface, pore size distribution, and surface area is of vital importance whenever quantitative data for processes occurring or starting at the surface of the carbon, such as surface reactions, adsorption, degassing, and surface treatment, are required.

[0003] Shaped carbon bodies are generally produced from powdered carbon particles with organic or inorganic binders. Carbon powder, binder, water, and other ingredients are mixed to form a material that is subsequently shaped. The shaped bodies of wet carbon/binder mixture must be thermally treated at high temperatures to increase product strength and water stability. For example, the prior art teaches using clay and phenolic resin polymer as binders. In particular, U.S. Pat. No. 4,677,086 to McCue et al. first disclosed the use of bentonite clay as a binder for powdered carbon, which disclosure is incorporated herein by reference. Subsequent improvements on this technology are disclosed in U.S. Pat. Nos. 5,204,310, 5,206,207, 5,238,470, 5,250,491, 5,276,000, 5,304,527, 5,538,932, 5,691,270, 5,736,481, 5,736,485, and 5,863,858, all assigned to Westvaco Corporation (hereafter, “the Westvaco patents”), the disclosures of which are incorporated herein by reference.

[0004] This prior art binder technology requires expensive plant equipment, is encumbered with a costly high temperature heat treatment step, and results in products which may fail to meet all required property characteristics for certain desired applications.

[0005] Also, other activated carbon binder technology includes U.S. Pat. No. 5,389,325 to Bookbinder et al., which describes activated carbon bodies having phenolic resin binder and describes a method to manufacture an extruded honeycomb that is water-resistant. Activated carbon powder was mixed with 5-35% phenolic resin and 4-10% organic plasticizer as an extrusion aid. The plasticizer was selected from a variety of cellulose derivatives. Thus, Bookbinder et al. teach inclusion of cellulose derivatives only as an extrusion aid in conjunction with phenolic resin as the binder material.

[0006] U.S. Pat. No. 4,866,023 to Ritter et al. discloses a process for the shaping agglomeration of particulate solids and solids produced by the process. The patentees claim a two-step process to granulate solid powders such as metal powders, insoluble metal salts, and activated carbons. Solid powders were first mixed with a polymeric binder and water to form a viscid mass that was shaped into droplets. The droplets were immediately immersed in a solution, which contained polyvalent cations such as Ca²⁺, Fe³⁺, Cu²⁺, etc. Water stability was obtained when the metal cations reacted with the polymer binder to form water-insoluble salts.

[0007] U.S. Pat. No. 4,920,090 to Ritter et al. discloses a process for the formation of shaped agglomerates from particulate solids and claims a binder system that improves the product thermal stability over U.S. Pat. No. 4,866,023. The previous cellulosic binder was replaced with polymers containing anhydrides of dicarboxylic acid. Metal cations were replaced with anhydride-reactivated polyamines. The same two-step manufacturing process was used.

[0008] In each case, the water stability of the prior art shaped carbon body was obtained by insolubilizing the polymer binders without a high-temperature treatment. Additionally, binders, crosslinking agents, or manufacturing processes were used other than as employed in the invention herein disclosed.

[0009] Finally, U.S. Pat. No. 4,215,096 to Sinha et al. teaches impregnating activated carbon with sodium hydroxide (NaOH) for use in purification of gas streams contaminated with acid and acid precursor gases and vapors.

BRIEF DESCRIPTION OF THE DRAWINGS

[0010]FIG. 1 is a general schematic of a prior art method of preparing clay-bound and phenolic resin-bound shaped activated carbon, for use in vapor adsorption applications.

[0011]FIG. 2 is a general schematic of a method of preparing a shaped activated carbon with an organic binder for use in vapor adsorption applications, with an option of including a functional promoter in the mixing step.

[0012]FIG. 3 is a general schematic of a method of preparing a shaped activated carbon with organic binder with or without post-impregnation with a functional promoter, for use in vapor adsorption applications.

[0013]FIG. 4 is a graphic representation of the effect on the butane working capacity (BWC) of a shaped activated carbon as a result of increasing content of phenolic resin as a binder.

[0014]FIG. 5 is a graphic representation of the effect on the apparent density (AD) of a shaped activated carbon as a result of increasing content of phenolic resin as a binder.

SUMMARY OF THE INVENTION

[0015] A binder for shaped activated carbon and a method for its manufacture have been discovered that do not require a costly high temperature heat treatment step. The inventive binder and inventive method of manufacturing shaped activated carbon comprise crosslinking of a polymeric binder, such as carboxymethylcellulose (CMC) and its derivative salts, within the activated carbon bodies after they are shaped. This approach to attain product mechanical strength and water stability by crosslinking, rather than high temperature heat treatment, is not obvious from the prior art. A crosslinking reaction occurs at temperatures up to about 270° C. In many instances, the crosslinking reaction can occur at temperatures of about 200° C. and below. In addition, this new binder technology produces shaped carbon bodies exhibiting properties beyond the best level that has been accomplished with other binders.

DESCRIPTION

[0016] As indicated in the embodiments of the invention represented by FIGS. 2 and 3, powdered activated carbon and a polymerizable organic binder chamber and combined with water, a base or an acid, and a crosslinking agent. The blend formed from such mixing can be shaped to form pellets, followed by drying and curing at temperatures up to about 270° C. A promoter may be added by either including it in the mixing step (FIG. 2) or impregnating it with formed pellets (FIG. 3).

[0017] The inventive binder provides shaped activated carbon with superior properties beyond the best level that has been accomplished with known shaped activated carbons made with a clay binder while maintaining similar values in other properties. An illustrative example is given for 2 mm×5 mm extruded pellets made from a Westvaco wood-based activated carbon. Compared to known (prior art) clay-bound pellets of the same size, the inventive polymeric binder-bound pellets made from the inventive method showed:

[0018] Retention of a greater gravimetric butane activity (75-85% vs. 60-70% of precursor carbon butane activity);

[0019] A lower apparent density (0.25-0.35 g/cc vs. 0.30-0.40 g/cc) so it requires less weight to fill the same volume;

[0020] A greater crush strength (2-8 kg/pellet vs. 2-4 kg/pellet) and abrasion hardness (values* of 75-100 vs. 60-85);

[0021] A lower initial dust (2-10 mg/dl vs. 15-40 mg/dl) and dust attrition rate (0.1-0.5 mg/dl/min vs. 1-3 mg/dl/min);

[0022] A lower ash content (<10% vs. ˜20%);

[0023] An equivalent volumetric butane working capacity (BWC) depending on precursor carbon butane adsorption capacity; and

[0024] An equivalent excellent water stability** of>95%.

[0025] An advantage of this new binder technology lies in the crosslinking of a polymerizable binder material, such as a polymeric cellulose (e.g., CMC), within the shaped carbon bodies after they are formed. By such crosslinking, the water-soluble CMC, for example, becomes insoluble in water and in many organic solvents including gasoline, toluene, tetrahydrofuran (THF), dimethylformamide (DMF), and formamide. The carbon bodies remain intact even after prolonged immersion in these liquids. Crosslinking of polymerizable binder, for example CMC, is achieved by its reactions with a polyfunctional crosslinking agent (CLA) such as, but not limited to, dimethylol urea melamine-formaldehyde, urea-formaldehyde, and polyamid-epichlorohydrin. The polyvalent minerals contained in activated carbons also serve as de facto crosslinking species under certain conditions. (They appear to be most effective at pH<7.) A base (such as sodium hydroxide) or acid (such as phosphoric acid) may be added in the mixing step to adjust the pH, which dictates the carbon body water stability and the desirability of adding a crosslinking agent. A typical formulation is as follows (all percentages are by weight, based on activated carbon, binder, and CLA):

[0026] Polymeric binders: Typically, at least about 3%, based on total dry solids weight, can be used. The upper limit of polymeric binder content depends on the need for product properties. In general, increasing polymeric binder content improves product mechanical characteristics but may reduce adsorptive capacity. A polymeric binder content of 2-15% typically is used for manufacturing shaped activated carbons for, for example, automotive adsorptive applications. A content of 4-8% can also be advantageously used;

[0027] CLA: A CLA content of up to 5.0% can be used, and a content of 0.5-1.5%, is typically used for complete crosslinking;

[0028] Water: Sufficient water is added to solubilize the polymerizable binder and saturate carbon porosity. Depending on the total pore volume of activated carbon and the polymerizable binder content, the final mix moisture content varies to obtain a mixture that is suitable for subsequent shaping;

[0029] Base: Sufficient base, such as sodium hydroxide, can be added to increase pH when binding activated carbons that are acidic, such as those manufactured by phosphoric acid activation. The pH can range from 4 to 10, and typically ranges from 5 to 9, and most often ranges from 6 to 8; and

[0030] Acid: Sufficient acid, such as phosphoric acid, can be added to reduce pH when binding activated carbons that are basic.

[0031] Useful organic polymerizable binders (i.e., crosslinkable by the same type of crosslinking agent) include, but are not limited to, carboxymethylcellulose (CMC) and its derivatives and its metal salts, guar gum cellulose, starch, lignin, polyvinyl alcohol, polyacrylic acid, styrene butadiene resins (SBR), and polystyrene acrylic acid resins. Water stable carbon bodies can also be made with crosslinked polyester network, including but not limited to those resulting from the reactions of polyacrylic acid or citric acid with different polyols such as glycerin, polyvinyl alcohol, lignin, and hydroxyethylcellulose.

[0032] Different types of shaped carbon bodies have been demonstrated with this inventive polymeric binder technology. These include (but are not limited to) granules, cylindrical pellets, spheres, sheets, ribbons, trilobes, and honeycombs. In principle, any desired shape of carbon body can be formed with a proper shaping device. So, shapes such as monoliths, blocks, and other modular forms are envisioned as well. This new binder technology is applicable to virtually all varieties of activated carbons, including those made from different precursor materials such as wood, coal, coconut, nutshell, and olive pit by acid, alkali, or thermal activation.

[0033] The inventive binder can work with a variety of mixing, shaping and heat treating equipment. Exemplary process schematics are shown in FIGS. 2 and 3. (For applications which do not require a functional promoter, its addition would not be included in FIG. 2, and no post-impregnation would be required in FIG. 3.) Different mixing devices such as low shear mullers, medium shear paddle mixers and high shear pin mixers have been demonstrated to produce a material that is suitable for subsequent shaping. Shaping devices such as auger extruders, ram extruders, granulators, roller pelletizers, spheronizers, and tabletting presses are suitable, depending on the applications. Drying and curing of the wet carbon bodies can be carried out at temperatures below 270° C. with a variety of different devices, such as a convection tray oven, a vibrating fluid bed dryer, and a rotary kiln. In contrast, higher temperatures of about 500-1000° C. must be used for prior art thermal treatment of clay-bound and phenolic resin-bound carbons, usually using a rotary kiln.

[0034] In one embodiment of the inventive process where the product application advantageously includes functional promoter addition, the functional promoter can be added during mixing of the activated carbon powder, binder, and other ingredients prior to shaping; thus, contrary to the teaching of U.S. Pat. No. 4,215,096, cited above, a separate post-impregnation is avoided. A schematic of this process embodiment is exemplified in FIG. 2. In this process embodiment, the binder system should not require a high temperature heat treatment that would cause the promoter to decompose, to become inactive, or to interact undesirably with the carbon or binder itself. Since pellets made by the invention binder technology are water stable, functional promoters may be added by the traditional post-impregnated method (FIG. 3) in another embodiment of the invention.

[0035] The advantages provided by the disclosed invention are apparent from and not limited to the following examples:

EXAMPLE 1

[0036] In existing commercial processes, an active component that promotes the adsorptive capacity or any other function of activated carbon is usually post-impregnated onto preformed carbon bodies. EXAMPLES of such commercial post-impregnation processes are noted below.

[0037] 1. In a commercial process to make carbon pellets, a functional promoter is impregnated onto pellets that are made with phenolic resin binder. Prior to impregnation, extruded pellets must be thermally treated at very high temperature (>850° C.) to attain the desired properties. (See, e.g., FIG. 1.)

[0038] 2. Calgon granular carbon impregnated with sodium hydroxide for removal of acidic contaminants from air streams, as disclosed in U.S. Pat. No. 4,215,096, cited above.

[0039] One disadvantage of the existing commercial method of promoter incorporation is that post-impregnation requires that the carbon body be stable in the aqueous solution and retain its strength after subsequent drying. In addition, post-impregnation adds one more operation step in the manufacturing process and, thus, increases product cost.

[0040] Examples in accordance with the present invention are provided in the table below, using a sodium salt as the functional promoter to make cellulosic polymer-bound pellets that are capable of capturing acidic contaminants such as H₂S. The sodium salt was added during mixing in one sample (FIG. 2) and by post-impregnation in the other sample (FIG. 3).

[0041] The CMC-bound carbon samples were prepared by grinding wood-based activated carbon and mixing the ground carbon with CMC as the binder and crosslinking agent. Sodium hydroxide was added for pH adjustment. In one experiment, functional promoter was added to the muller, as noted. Sufficient water was added to make the mixture rheology suitable for screw auger extrusion. The final mixture was shaped to 4.6 mm pellets by a pilot Bonnot extruder. The green pellets were tumbled, dried, and cured at 100-200° C. When the promoter was not added to the muller, the cured pellets were impregnated with the promoter in an aqueous solution, following the same procedure for impregnation of phenolic resin-bound pellets. TABLE I Comparison of Specialy Carbon (for Acid Gas Removal) Properties Binder Phenolic Resin CMC Promoter added Post- Mixing Post- impregnation addition impregnation Promoter content 9.9% 9.5% 10.4% pH 10-11 10.7 10.9 H2S performance >95% >95% >95% AD (g/cc, db) 0.39-0.40 0.39 0.39 Water stability >95% >95% >95% Initial dust (mg/dl)  5-10 0.7 1.8 Dust Attrition (mg/dl/min) 0.2-2   0.03 0.07 Pellet strength 70-85 74 74 Mean particle diameter (mm) 4.4-4.7 4.6 4.5

[0042] Compared with the traditional plant-produced phenolic resin-bound carbon, the invention cellulosic polymer-bound counterparts showed: a) similar, maybe slightly better, H₂S adsorption performance; b) significantly lower initial dust and dust attrition rate; and c) similar density and mechanical strength.

EXAMPLE 2

[0043] This example is provided to show the benefits of the disclosed invention product and processes in the use of a polymerizable cellulose as the binder additive (in the absence of phenolic resin), as compared to using phenolic resin as the activated carbon binder with carboxymethylcellulose merely as a plasticizing extrusion aid, as taught in U.S. Pat. No. 5,389,325, cited above. These benefits are graphically depicted in FIGS. 4 and 5.

[0044] The data, as graphically depicted in FIGS. 4 and 5, clearly indicate the benefits of the invention herein disclosed. As the phenolic resin content was increased, the BWC decreased markedly and the density increased. Even with as little as 5% phenolic resin, the BWC was still 0.5 g/dL below the invention product BWC value.

EXAMPLE 3

[0045] Shaped activated carbon (2 mm), manufactured and sold by Westvaco Corporation for automotive emission control is made with bentonite clay as a binder (made as disclosed in one or more of the Westvaco patents, cited earlier). The patents teach the necessity of a very high temperature treatment. Similar carbon samples were made according to the schematic of FIG. 2, without inclusion of any functional promoter. The commercial samples and invention samples were measured for ash content, and the results are shown in Table II. TABLE II Ash Contents of CMC-Bound and Clay-Bound Shaped Activated Carbons Samples A B C Binder Plant-made Pilot-made Pilot-made Average Commerical (Clay) 25.3% 23.3% 23.8% 24.1% Invention (CMC) 7.2% 6.5% 7.2% 7.0%

[0046] As shown in Table II, the CMC-bound carbon samples have an average ash content of about 7.0% vs. 24.1% for the clay-bound carbons. Thus, the new CMC binder yields a product containing less ash (<10%) than clay binder. The ash content was determined by the weight reduction after 3 hours of combustion at ˜650° C. in a muffle furnace (ASTM D2866-94[1999]).

EXAMPLE 4

[0047] In order to show the performance comparisons of CMC-bound shaped activated carbon bodies (pellets) with prior art shaped activated carbon bodies (pellets) of the same size, samples of shaped activated carbon pellets were made using each type of binder material, and their properties were measured. Clay-bound samples were prepared according to the process described in U.S. Pat. No. Pat. No. 4,677,086, mentioned above. The phenolic resin-based samples were prepared according to the process described in U.S. Pat. No. 5,736,485 mentioned above, which process includes a green pellet (newly formed pellet) tumbling step to reduce initial dust, as well as the pellet dust rate. The inventive CMC-bound samples were prepared as set forth and claimed herein (but without functional promoter addition). The measured properties of each sample are set forth in the following Table III. TABLE III CMC vs. Clay & Phenolic as Binder Material for Shaped Activated Carbon Butane Water Initial Dust AD Activity BWC Stability Dust Rate Binder g/ml g/100 g g/DL pH % Hardness mg/dL mg/dL/min Clay 0.36 39.5 11.9 7.4 98 81 22.2 0.55 CMC 0.33 43.2 12 1 5.8 96 94 7.4 0.10 Phenolic 0.40 28.8  9.8 6.2 96 99 5.5 0.07

[0048] The properties of the sample prepared with the polymeric cellulosic binder were essentially equal or were better than the samples prepared according to the prior art. The CMC-bound shaped activated carbon pellets had acceptable apparent density (AD), pH, water stability, and hardness, and exhibited improved activity (both butane activity and butane working capacity (BWC). While the initial dust and dust rate values were essentially equivalent to the phenolic-bound sample, those values were much improved in comparison to the clay-bound sample.

[0049] Although a benefit of the disclosed process is to provide an option to include any functional promoter in the initial mixing step, where such activity in the activated carbon product is desired (and avoid a separate post-treatment step), the disclosed invention includes various optional post-treatments to fashion the shaped activated carbon product for specialized applications. Such post-treatments may, among others, include:

[0050] (1) Thermal treatment in the presence of agents such as chlorine or silicon-halogen drerivatives to render the carbon surface hydrophobic for capture of chemical species in humid atmospheres (e.g., for use in respirators, solvent recovery, vehicle exhaust);

[0051] (2) Thermal treatment in the presence of nitrogen-containing agents (ammonia, heterocyclics, hydrogen cyanide, nitrogen, urea) to incorporate nitrogen into the carbon structure and thereby impart catalytic activity for electron exchange reactions (e.g., production of glyphosate herbicide);

[0052] (3) Conversely, thermal treatment in hydrogen to block edge carbon atoms, thereby rendering the carbon surface largely non-reactive;

[0053] (4) Impregnation with phosphoric acid and/or derivatives of phosphoric acid, followed by thermal treatment to produce catalyst products for hydrodehalogenation and hydrodesulfurization reactions;

[0054] (5) Impregnation of the bound carbon with chemically reactive species, such as alkalis, alkali salts, sulfur, to impart activity for capture of pollutants through chemical reactions and/or chemisorption (e.g., capture of VOC's, H₂S, mercaptans, mercury);

[0055] (6) Impregnation with, and subsequent thermal treatment of, noble metal salts (e.g., of platinum, palladium) to produce carbon-supported catalysts for a wide range of applications. Similar treatment with salts of vanadium, molybdenum;

[0056] (7)Thermal treatment in ozone to oxidize the surface and enhance hydrophilicity and reactivity. Treatment with other oxidants for the same purpose, such as HNO₃ and H₂O₂;

[0057] (8) Production of molecular sieve products through thermal treatment of the CMC-bound carbon in the presence of hydrocarbons (e.g., benzene, toluene) to crack the hydrocarbon and deposit carbon in the porosity of the bound-carbon, thereby narrowing pore diameter; and

[0058] (9) Impregnation with urea, potassium, and/or phosphates, and subsequent thermal treatment if desirable, to produce controlled-release fertilizers. Similar application for controlled-release pesticides.

[0059] While the invention has been described above with reference to specific embodiments thereof, it will be apparent to skilled persons that minor changes, modifications, and variations may be made to the details of the invention described herein without departing from the underlying principles of the inventive concept disclosed, including various obvious substitutions, such as substitute pH-modifying acids and/or bases. Nevertheless, the subject matter of the invention is within the bounds of the following claims. 

What is claimed is:
 1. A method for preparing a shaped activated carbon body comprising the steps of (a) blending powdered activated carbon, a polymeric binder, a solvent, a pH modifier, and a crosslinking agent in a mixer to produce a blended material; (b) shaping the blended material; and (c) drying the shaped blended material at a temperature up to 270° C.
 2. The method of claim 1 wherein the blended material is comprised of 2-30% polymeric binder, up to 5.0% crosslinking agent, sufficient pH modifier to adjust the pH of the blended material to a pH of 4-10, and sufficient solvent to solubilize the polymeric binder, wherein percentages are by weight, based on the total dry weight of the activated powdered carbon, binder, and crosslinking agent.
 3. The method of claim 2 wherein the blended material is comprised of 4-8% polymeric binder, 0.5-1.5% crosslinking agent, sufficient pH modifier to adjust the pH of the blended material to a pH of 5-9.
 4. The method of claim 3 wherein the blended material is comprised of sufficient pH modifier to adjust the blended material to a pH of 6-8.
 5. The method of claim 1 further comprising in the blending step (a), a functional promoter.
 6. The method of claim 1 wherein the polymeric binder is selected from the group of sodium carboxymethylcellulose, guar gum cellulose, starch, lignin, polyvinyl alcohol, polyacrylic acid, styrene butadiene resins (SBR), polystyrene acrylic acid resins, and reaction products of polyacrylic acid with polyols selected from the group of glycerin, polyvinyl alcohol, lignin, and hydroxyethylcellulose.
 7. The method of claim 6 wherein the polymeric binder is sodium carboxymethylcellulose.
 8. The method of claim 1 wherein the shaped product of step (b) is in the form of shapes including granules, cylindrical pellets, trilobes, spheres, sheets, ribbons, honeycombs, monoliths, and blocks.
 9. The method of claim 1 wherein the blending of step (a) is conducted in equipment selected from a low shear mixer, a medium shear mixer, and a high shear pin mixer, and wherein the shaping of step (b) is conducted in equipment selected from an auger extruder, a granulator, a roller pelletizer, a ram extruder, a spherinizer, and a tabletting press.
 10. The method of claim 1 wherein step (c) is conducted at a temperature up to about 200° C.
 11. The method of claim 5 wherein the functional promoter is sodium hydroxide, potassium hydroxide, sodium carbonate, potassium carbonate, calcium carbonate, and magnesium carbonate.
 12. The method of claim 1 further comprising step (d) heating the dried shaped activated carbon body in the presence of an agent selected from chlorine, silicon-halogen derivatives, nitrogen-containing agents, hydrogen, hydrocarbons, and oxidants.
 13. The method of claim 12 wherein the nitrogen-containing agents are selected from ammonia, heterocyclics, hydrogen cyanide, nitrogen, and urea, wherein the oxidants are selected from ozone, HNO₃, and H₂O₂, and wherein the hydrocarbons are selected from benzene and toluene.
 14. The method of claim 1 wherein the solvent is water or an organic solvent.
 15. The method of claim 1 further comprising step (d) impregnating the dried shaped activated carbon body with a solution of a sufficient amount of phosphoric acid, a derivative of phosphoric acid, or a mixture thereof to impart catalytic activity for hydrodehalogenation and hydrodesulfurization reactions; and step (e) drying the impregnated shaped activated carbon body.
 16. The method of claim 1 further comprising step (d) impregnating the dried shaped activated carbon body with a solution of a sufficient amount of an alkali, an alkali salt, or sulfur to impart antipollutant properties to said carbon body; and step (e) drying the impregnated shaped activated carbon body.
 17. The method of claim 1 further comprising step (d) impregnating the dried shaped activated carbon body with a solution of a sufficient amount of a salt of platinum, palladium, vanadium, or molybdenum to produce a carbon-supported catalyst; and step (e) drying the impregnated shaped activated carbon body. 